In this study, AKF-78 grade Angren kaolin was used to synthesize KA zeolite. The obtained metakaolin and KCl were mixed in a 1:1 molar ratio. The prepared mixture was treated with a 2M NaOH solution and heated in an autoclave for 28 hours at 100°C. Based on the XRD data of the KA zeolite obtained through hydrothermal synthesis, it was compared with the peaks of LTA zeolite crystals. The KA zeolite synthesized from Angren kaolin through hydrothermal synthesis was found to fully correspond to the formula Al10H72K4.63Na6O91.32Si25.38 based on the XRD data. Furthermore, it was determined that the KA zeolite consists of the following elemental composition: O-51.2%, Si-25%, Al-10%, K-6.3%, Na-4.8%, and H-2.5%. The degree of crystallization and amorphicity of the zeolite was also determined. The degree of crystallization of KA zeolite was found to be 29.09%, while the degree of amorphicity was 70.91%. In the analysis of the catalytic or adsorption properties of the zeolites, crystal sizes are of significant importance. The LTA zeolite and the synthesized KA zeolite were compared using X-ray diffraction (XRD).
| Mualliflar | Mukhammadjonov, Mirjalol, Rakhmatkarieva, Firuza, Oydinov, Mukhlis |
|---|---|
| Jurnal | Наманган муҳандисликтехнология институти илмийтехника журнали |
| Nashr sanasi | 2025-03-31 |
| Jild | 10 |
| Son | 1 |
| Betlar | 153-159 |
| Til | Ingliz |
| DOI | 10.61151/stjniet.v10i1.732 |
DOI: 10.61151/stjniet.v10i1.732 · Maqolaning asl sahifasi
Metakaolin, nanostructure, zeolite, kaolin, crystal, X-ray, hydrothermal, autoclave, diffraction, amorphous
This study investigates the physicochemical properties of phenol-formaldehyde resin (PFR) and polystyrene (PS) waste as promising secondary resources for the production of carbon-based adsorbents. A comparative analysis…
The synthesis, characterization, and physicochemical characteristics of water-soluble methylated chitosan derivatives are the main topics of this research. There are several uses for trimethylchitosan and…
In this article, the chemical composition of products obtained by decomposing two differently composed samples of Central Kyzylkum phosphorite using industrial waste sulfuric acid was studied. During the research, the…
This article presents the experimentally obtained values of differential enthalpy of ammonia adsorption at 303 K in Ca4Na4A (Horst-50/50) zeolite of the LTA type. The enthalpy values were measured using a modified…
In this article, samples of cotton fibers (selected industrial grades such as S-65-24 I/1, Bukhara-102 I/1, and Andizhan-36 I/1), obtained in the ginning process after the newly created regeneration of cotton linters in…
This article presents the experimentally obtained values of the adsorption isotherm of ammonia molecules on zeolitite СаА (MSS-622) at a temperature of 303 K. The isotherm was measured using a DAC-1-1A microcalorimeter…
The article theoretically analyzes the forces affecting the seed flow during transportation of cotton seeds by bucket elevators. It also analyzes the influence of technological parameters on seed damage. The theoretical…
Plants from which oil is extracted include cotton, soybeans, sunflowers, peanuts, safflower, corn, olives, and sesame. Currently, the most common method for industrially extracting cottonseed oil is by pressing…
The aim of this study is to determine the amygdalin content in peach oil obtained using the pressing method. This information is crucial for evaluating the quality of peach oil and expanding its potential applications…
This article discusses the current state of the global textile industry, including the volume of textile product manufacturing in developed countries, the size of the European textile market, and issues such as…
Наманган муҳандисликтехнология институти илмийтехника журнали — barcha maqolalar