The aim of the work was to obtain high-density optically transparent ceramic samples by sintering cubic modification Er2O3 and Yb2O3 oxides micropowders at the pressure of 7 GPa and the heating current power of 0.6–1.0 kW, which was demonstrated. Non-monotonic dependence of the density on the heating current power has been established. The maximum density values of 9.2 g/cm3 (Er2O3) and 9.8 g/cm3 (Yb2O3) were achieved at the power of 0.8 and 0.9 kW, respectively. During sintering, the cubic phase partially transforms into the monoclinic phase, which is preserved in the obtained samples. The ceramics compaction process is accompanied by grain growth, more intense in erbium oxide samples. At sintering Yb2O3 micro-powder with particle size of 7.5–15 μm with the lowest heating current power value of 0.6 kW a microstructure similar to the nanocrystalline with the grain size of 90–200 nm, which contributes to higher transparency in the infrared wavelength range. Er2O3 samples have a discontinuous transmission spectrum, while Yb2O3 samples – a continuous one in the wavelength range of 400–850 nm. The maximum transmission values for ceramic samples are 29% at a wavelength of 750 nm, 52% at 849 nm for Er2O3 and 72% at 830 nm for Yb2O3.
| Mualliflar | В. С. Урбанович, V. D. Zhivulko, Е. Н. Подденежный, Е. Е. Трусова, В. С. Нисс |
|---|---|
| Jurnal | Kimyo va kimyo texnologiyasi |
| Nashriyot | Тошкент кимё-технология институти |
| ISSN | 1992-9498, 2181-1121 |
| Nashr sanasi | 2025-12-01 |
| Jild | 2025 |
| Son | 4 |
| Til | Ingliz |
| DOI | 10.70189/1992-9498.1687 |
| Indeksga qo‘shilgan | 2026-09-02 |
DOI: 10.70189/1992-9498.1687 · Maqolaning asl sahifasi · PDF
| APA | В. С. Урбанович, V. D. Zhivulko, Е. Н. Подденежный, Е. Е. Трусова, & В. С. Нисс (2025). THE STRUCTURE AND PROPERTIES OF Er2O3 AND Yb2O3 BASED CERAMIC MATERIALS, SINTERED UNDER HIGH PRESSURE. Kimyo va kimyo texnologiyasi, 2025(4). https://doi.org/10.70189/1992-9498.1687 |
|---|---|
| GOST (OAK) | В. С. Урбанович va b. THE STRUCTURE AND PROPERTIES OF Er2O3 AND Yb2O3 BASED CERAMIC MATERIALS, SINTERED UNDER HIGH PRESSURE // Kimyo va kimyo texnologiyasi. – 2025. – T. 2025, № 4. – DOI: 10.70189/1992-9498.1687. |
| MLA | В. С. Урбанович, V. D. Zhivulko, Е. Н. Подденежный, Е. Е. Трусова, and В. С. Нисс. “THE STRUCTURE AND PROPERTIES OF Er2O3 AND Yb2O3 BASED CERAMIC MATERIALS, SINTERED UNDER HIGH PRESSURE.” Kimyo va kimyo texnologiyasi, 2025(4), 2025. https://doi.org/10.70189/1992-9498.1687 |
| Chicago | В. С. Урбанович, V. D. Zhivulko, Е. Н. Подденежный, Е. Е. Трусова, and В. С. Нисс. “THE STRUCTURE AND PROPERTIES OF Er2O3 AND Yb2O3 BASED CERAMIC MATERIALS, SINTERED UNDER HIGH PRESSURE.” Kimyo va kimyo texnologiyasi, 2025(4) (2025). https://doi.org/10.70189/1992-9498.1687 |
| Harvard | В. С. Урбанович, V. D. Zhivulko, Е. Н. Подденежный, Е. Е. Трусова, and В. С. Нисс (2025) ‘THE STRUCTURE AND PROPERTIES OF Er2O3 AND Yb2O3 BASED CERAMIC MATERIALS, SINTERED UNDER HIGH PRESSURE’, Kimyo va kimyo texnologiyasi, 2025(4). https://doi.org/10.70189/1992-9498.1687 |
| BibTeX | @article{article2025,
title = {THE STRUCTURE AND PROPERTIES OF Er2O3 AND Yb2O3 BASED CERAMIC MATERIALS, SINTERED UNDER HIGH PRESSURE},
author = {В. С. Урбанович and V. D. Zhivulko and Е. Н. Подденежный and Е. Е. Трусова and В. С. Нисс},
journal = {Kimyo va kimyo texnologiyasi},
year = {2025},
volume = {2025},
number = {4},
doi = {10.70189/1992-9498.1687},
url = {https://doi.org/10.70189/1992-9498.1687}
} |
Boshqa maqola uchun iqtibos tayyorlash
The aim of the work is to study the transformations of quartz raw materials as a result of high-temperature exposure. The objects of the study were quartzite from the Dzherdanak deposit in the Surkhandarya region and…
The aim of this study is to perform quantum-chemical modeling of mixed-ligand complexes of trivalent lanthanoid ions (Ln³⁺) involving primary ligands — 2-amino-1-methylbenzimidazole (MAB) and…
In this study we aimed to obtain a novel recombinant β-galactosidase baculovirus using the Bombyx mori baculovirus – insect cell expression system. A new recombinant plasmid was constructed on the basis of the pBacPAK8…
The primary objective of this study is to optimize the process of isolating the C9 hydrocarbon fraction from pyrolysis distillate and to evaluate the impact of various temperature regimes on the product composition. To…
The purpose of this study is to analyze the chemical, mineralogical, and fractional composition of sylvinite from the Khodjaikan deposit in Uzbekistan in order to assess its potential for potassium fertilizer…
Titanium is classified as a critical metal. It serves as a raw material for a wide range of industries owing to its unique properties – high strength at low density, corrosion resistance, and biocompatibility makes it…
The aim of this study was to produce lightweight thermal insulation bricks based on Djerdanak clay shale with the addition of wood sawdust. The starting materials were clay shale from the Djerdanak deposit, fireclay…
The aim of study is synthesize mixed oxide composites based on titanium dioxide, iron and molybdenum oxides from industrial waste materials and evaluated for their photocatalytic degradation performance of…
The aim of the work is to find ways to use cryotic metals that also provide added value to the economy, using the example of tantalum and zirconium. Among the critical metals, there are those that are rarely found in…
A comprehensive physicochemical study of the aqueous “urea – glycine” system was conducted to establish the mechanisms of intermolecular interaction and stability parameters for the development of modified liquid…
Kimyo va kimyo texnologiyasi — barcha maqolalar · 2025-yil arxivi