Synthesis of nanostructured cerium-doped yttrium-aluminum garnets by method of sol-gel burning in a microwave oven

Е. Н. Подденежный, Andrei A. BOIKO, Е. Е. Трусова, Ekaterina R. KRAVCOVA

Kimyo va kimyo texnologiyasi · 2024-yil

Annotatsiya

The aim of research is to study the new method of thermochemical synthesis of yttrium-aluminum garnet luminescent powder, cerium doped (Y3Al5O12:Се3+, YAG:Ce) using the nitric acid salts of yttrium, aluminum and cerium, with the mixture of carbamide and hexamethylenetetramine used as fuel. Synthesis was performed in a microwave oven with the power of 800 W and frequency of 2450 MHz in a porcelain crucible closed with a perforated heat-resistant cover. The average size of coherent scattering region (CSR) of YAG:Ce particles (nominal diameter D) obtained in the crucible during the microwave heating is 50.3 nm. It has been established that when YAG powder is produced by burning, the reaction cup reaches the temperature sufficient for Y3Al5O12 compound synthesis, and that the reducing environment arising due to the combustion of the organic mixture contributes to formation of Ce ions in tricharged state. Further calcination of the resulting powder at the temperature of 450, 900 and 1100 ºC in the open air leads to formation of practically single-phase YAG structure. The radiation spectrum of the obtained YAG:Ce luminescent powders has a wide bandwidth caused by the energy transitions of Ce3+ ion in the garnet structure between 490 and 750 nm at LED excitation at 450 nm. It corresponds to yellow-green radiation that with blue LED radiation creates the sensation of white light. The highest intensity of the yellow-green luminescence is reached by the YAG:Ce powders calcinated at 900 ºC in the open air.

Maqola ma’lumotlari
MualliflarЕ. Н. Подденежный, Andrei A. BOIKO, Е. Е. Трусова, Ekaterina R. KRAVCOVA
JurnalKimyo va kimyo texnologiyasi
NashriyotТошкент кимё-технология институти
ISSN1992-9498, 2181-1121
Nashr sanasi2024-09-27
Jild2024
Son3
TilIngliz
Ilmiy sohaKimyo
DOI10.70189/1992-9498.1624
Indeksga qo‘shilgan2026-09-02

DOI: 10.70189/1992-9498.1624 · Maqolaning asl sahifasi · PDF

Ilmiy soha

Kimyo

Iqtibos keltirish

APAЕ. Н. Подденежный, Andrei A. BOIKO, Е. Е. Трусова, & Ekaterina R. KRAVCOVA (2024). SYNTHESIS OF NANOSTRUCTURED CERIUM-DOPED YTTRIUM-ALUMINUM GARNETS BY METHOD OF SOL-GEL BURNING IN A MICROWAVE OVEN. Kimyo va kimyo texnologiyasi, 2024(3). https://doi.org/10.70189/1992-9498.1624
GOST (OAK)Е. Н. Подденежный va b. SYNTHESIS OF NANOSTRUCTURED CERIUM-DOPED YTTRIUM-ALUMINUM GARNETS BY METHOD OF SOL-GEL BURNING IN A MICROWAVE OVEN // Kimyo va kimyo texnologiyasi. – 2024. – T. 2024, № 3. – DOI: 10.70189/1992-9498.1624.
MLAЕ. Н. Подденежный, Andrei A. BOIKO, Е. Е. Трусова, and Ekaterina R. KRAVCOVA. “SYNTHESIS OF NANOSTRUCTURED CERIUM-DOPED YTTRIUM-ALUMINUM GARNETS BY METHOD OF SOL-GEL BURNING IN A MICROWAVE OVEN.” Kimyo va kimyo texnologiyasi, 2024(3), 2024. https://doi.org/10.70189/1992-9498.1624
ChicagoЕ. Н. Подденежный, Andrei A. BOIKO, Е. Е. Трусова, and Ekaterina R. KRAVCOVA. “SYNTHESIS OF NANOSTRUCTURED CERIUM-DOPED YTTRIUM-ALUMINUM GARNETS BY METHOD OF SOL-GEL BURNING IN A MICROWAVE OVEN.” Kimyo va kimyo texnologiyasi, 2024(3) (2024). https://doi.org/10.70189/1992-9498.1624
HarvardЕ. Н. Подденежный, Andrei A. BOIKO, Е. Е. Трусова, and Ekaterina R. KRAVCOVA (2024) ‘SYNTHESIS OF NANOSTRUCTURED CERIUM-DOPED YTTRIUM-ALUMINUM GARNETS BY METHOD OF SOL-GEL BURNING IN A MICROWAVE OVEN’, Kimyo va kimyo texnologiyasi, 2024(3). https://doi.org/10.70189/1992-9498.1624
BibTeX
@article{article2024,
  title = {SYNTHESIS OF NANOSTRUCTURED CERIUM-DOPED YTTRIUM-ALUMINUM GARNETS BY METHOD OF SOL-GEL BURNING IN A MICROWAVE OVEN},
  author = {Е. Н. Подденежный and Andrei A. BOIKO and Е. Е. Трусова and Ekaterina R. KRAVCOVA},
  journal = {Kimyo va kimyo texnologiyasi},
  year = {2024},
  volume = {2024},
  number = {3},
  doi = {10.70189/1992-9498.1624},
  url = {https://doi.org/10.70189/1992-9498.1624}
}

Boshqa maqola uchun iqtibos tayyorlash

Kimyo va kimyo texnologiyasi jurnalidan boshqa maqolalar

Kimyo va kimyo texnologiyasi — barcha maqolalar · 2024-yil arxivi

Kimyo sohasidagi boshqa maqolalar

Kimyo sohasidagi OAK jurnallari