W-Cu-Co-C tizimli materialni yuqori termobarik ishlov berish orqali olingan kompozitni mexanik va elektrofizik xossalari

Muxamedova, Ziyoda, Ignatenko, Oleg, Fayzibayev, Sherzod, Tursunov, Toxir, Urazbayev, Talgat, Mamayev, Sherali, Mukhamedova, Ziyoda, Ignatenko, Oleg, Fayzibaev, Sherzod, Tursunov, Tokhir, Urazbaev, Talgat, Mamaev, Sherali

ТАЙИ хабарномаси · 2025-yil

Annotatsiya

Ushbu tadqiqot volfram karbidi-kobalt (WC-Co) tizimida sementlangan karbidlarini yuqori bosim vayuqori harorat (YuBH) sharoitida sintez qilishning yangi usulini taklif etadi. Tadqiqotning maqsadi buushbu ikki komponentli tizimda qattiqlik va mustahkamlik o‘rtasidagi bog‘liqlik muvozanatmuammosini bartaraf etishdan iborat. WC-Co kompozitlari termobarik sharoitlarda ya’ni 4~8 GPa va1200~2200 °C harorat intervalida elementar volfram, uglerod va kobaltdan to‘g‘ridan-to‘g‘ri sintez yo‘libilan tashkil qilinib olinib, bunda WC fazasining hosil bo‘lishi va zichlanishning bir bosqichda amalgaoshishiga imkon berdi. Strukturaviy XRD, SEM va TEM kabi tahlillardan so‘ng, mexanik sinovlaro‘tilgan boshqich natijalari maqolada aks ko‘rsatilgan. Mexanik sinovlardan - qattiqlikga, qovushqoqsinishga, ishqalanishga bardoshlilikga va elektrofizik xossalardan – elektr qarshilikga va magnitto‘yinganlik kabi parametrlar uchun bajarilgan. Yuqori bosim va haroratda olingan WC-Co kompozitlar13~15 GPa qattiqlik va 12~14 MPa·m½ qovushqoq sinishga chidamlilik ko‘rsatkichlariga erishilib ishlabchiqarishda keng qo‘llanadigan WC-6Co sinfiga xos bo‘lgan qiymatlardan, ya’ni 12~14 GPa qattiqlik va8~11 MPa·m½ qovushqoqlik kabi ko‘tsatgichlardan yuqoridir. Natijalar shuni ko‘rsatadiki, YUBHsintezi kompozit materialning yuqori zichlikka erishishini ko‘rsatib, bir xil tarkibli WC-Co materiallariniyuqori mexanik xossalar va issiqlikka bardoshlikni hosil qiladi va an’anaviy sinterlash texnologiyasigasamarali alternativ jarayon sifatida taklif etilishi mumkin.

Maqola ma’lumotlari
MualliflarMuxamedova, Ziyoda, Ignatenko, Oleg, Fayzibayev, Sherzod, Tursunov, Toxir, Urazbayev, Talgat, Mamayev, Sherali, Mukhamedova, Ziyoda, Ignatenko, Oleg, Fayzibaev, Sherzod, Tursunov, Tokhir, Urazbaev, Talgat, Mamaev, Sherali
JurnalТАЙИ хабарномаси
NashriyotТошкент автомобиль йўлларини лойиҳалаш, қуриш ва эксплуатацияси институти
ISSN2181-2438, 3060-5164
Nashr sanasi2025-12-30
Jild2
Son4
Betlar252-257
TilO‘zbek
Ilmiy sohaTexnika
DOI10.56143/2181-2438-2025-4-252-257
Indeksga qo‘shilgan2026-08-26

DOI: 10.56143/2181-2438-2025-4-252-257 · Maqolaning asl sahifasi

Kalit so‘zlar

thermobaric synthesis, WC-Co composites, high-pressure-high-temperature (HPT) process, phase formation, cemented, carbides, mechanical properties, mechanical tests, electrophysical properties, termobarik sintez, WC-Co kompozitlari, yuqori bosim-yuqori harorat (YuBH) jarayoni, faza hosil bo‘lishi, sementitlangan, karbidlar, mexanik xossalari, mexanik sinovlar, elektrofizik xossalar

Ilmiy soha

Texnika

Iqtibos keltirish

APAMuxamedova, Ziyoda, Ignatenko, Oleg, Fayzibayev, Sherzod, Tursunov, Toxir, Urazbayev, Talgat, Mamayev, Sherali, Mukhamedova, Ziyoda, Ignatenko, Oleg, Fayzibaev, Sherzod, Tursunov, Tokhir, Urazbaev, Talgat, & Mamaev, Sherali (2025). W-Cu-Co-C tizimli materialni yuqori termobarik ishlov berish orqali olingan kompozitni mexanik va elektrofizik xossalari. ТАЙИ хабарномаси, 2(4), 252-257. https://doi.org/10.56143/2181-2438-2025-4-252-257
GOST (OAK)Muxamedova, Ziyoda va b. W-Cu-Co-C tizimli materialni yuqori termobarik ishlov berish orqali olingan kompozitni mexanik va elektrofizik xossalari // ТАЙИ хабарномаси. – 2025. – T. 2, № 4. – B. 252-257. – DOI: 10.56143/2181-2438-2025-4-252-257.
MLAMuxamedova, Ziyoda, Ignatenko, Oleg, Fayzibayev, Sherzod, Tursunov, Toxir, Urazbayev, Talgat, Mamayev, Sherali, Mukhamedova, Ziyoda, Ignatenko, Oleg, Fayzibaev, Sherzod, Tursunov, Tokhir, Urazbaev, Talgat, and Mamaev, Sherali. “W-Cu-Co-C tizimli materialni yuqori termobarik ishlov berish orqali olingan kompozitni mexanik va elektrofizik xossalari.” ТАЙИ хабарномаси, 2(4), 252-257, 2025. https://doi.org/10.56143/2181-2438-2025-4-252-257
ChicagoMuxamedova, Ziyoda, Ignatenko, Oleg, Fayzibayev, Sherzod, Tursunov, Toxir, Urazbayev, Talgat, Mamayev, Sherali, Mukhamedova, Ziyoda, Ignatenko, Oleg, Fayzibaev, Sherzod, Tursunov, Tokhir, Urazbaev, Talgat, and Mamaev, Sherali. “W-Cu-Co-C tizimli materialni yuqori termobarik ishlov berish orqali olingan kompozitni mexanik va elektrofizik xossalari.” ТАЙИ хабарномаси, 2(4), 252-257 (2025). https://doi.org/10.56143/2181-2438-2025-4-252-257
HarvardMuxamedova, Ziyoda, Ignatenko, Oleg, Fayzibayev, Sherzod, Tursunov, Toxir, Urazbayev, Talgat, Mamayev, Sherali, Mukhamedova, Ziyoda, Ignatenko, Oleg, Fayzibaev, Sherzod, Tursunov, Tokhir, Urazbaev, Talgat, and Mamaev, Sherali (2025) ‘W-Cu-Co-C tizimli materialni yuqori termobarik ishlov berish orqali olingan kompozitni mexanik va elektrofizik xossalari’, ТАЙИ хабарномаси, 2(4), 252-257. https://doi.org/10.56143/2181-2438-2025-4-252-257
BibTeX
@article{muxamedovaziyoda2025,
  title = {W-Cu-Co-C tizimli materialni yuqori termobarik ishlov berish orqali olingan kompozitni mexanik va elektrofizik xossalari},
  author = {Muxamedova, Ziyoda and Ignatenko, Oleg and Fayzibayev, Sherzod and Tursunov, Toxir and Urazbayev, Talgat and Mamayev, Sherali and Mukhamedova, Ziyoda and Ignatenko, Oleg and Fayzibaev, Sherzod and Tursunov, Tokhir and Urazbaev, Talgat and Mamaev, Sherali},
  journal = {ТАЙИ хабарномаси},
  year = {2025},
  volume = {2},
  number = {4},
  pages = {252-257},
  doi = {10.56143/2181-2438-2025-4-252-257},
  url = {https://doi.org/10.56143/2181-2438-2025-4-252-257}
}

Boshqa maqola uchun iqtibos tayyorlash

ТАЙИ хабарномаси jurnalidan boshqa maqolalar

ТАЙИ хабарномаси — barcha maqolalar · 2025-yil arxivi

Muxamedova, Ziyoda — boshqa maqolalari

Texnika sohasidagi boshqa maqolalar

Texnika sohasidagi OAK jurnallari